Effect of the sintering method on microstructure and thermal and mechanical properties of zirconium oxophosphate ceramics Zr 2 O(PO 4 ) 2

Abstract : Due to an ultra-low thermal expansion, Zr2O(PO4)2 could find many applications as a thermal shock resistant material. To this end, ceramic processing is a key step in order to reach best properties. In this work, Zr2O(PO4)2 was sintered by conventional sintering and by the spark plasma sintering technique (SPS) with and without additive. Samples made by conventional sintering with ZnO as sintering aid have a maximum relative density of around 92 %. Microstructure is composed of large grains and microcracks can be observed. When doped 2 with 5 wt. % of MgO, samples can be densified by SPS up to 99.6 % of the relative density and the grain size maintained between 0.5 and 1.5 μm. Thermal conductivity and Vickers microhardness were investigated as a function of the microstructure. Best values were obtained for the ceramic doped with 5 wt.% MgO and sintered by SPS, thanks to a fine microstructure and a small amount of residual microcracks.
Type de document :
Article dans une revue
Journal of Physics and Chemistry of Solids, Elsevier, 2017, 111, pp.304-310. 〈10.1016/j.jpcs.2017.08.008〉
Liste complète des métadonnées

Littérature citée [21 références]  Voir  Masquer  Télécharger

http://hal.upmc.fr/hal-01590780
Contributeur : Gestionnaire Hal-Upmc <>
Soumis le : mercredi 20 septembre 2017 - 11:31:54
Dernière modification le : jeudi 11 janvier 2018 - 06:27:53

Fichier

 Accès restreint
Fichier visible le : 2018-02-10

Connectez-vous pour demander l'accès au fichier

Identifiants

Collections

Citation

Damien Bregiroux, Julie Cedelle, Isabelle Ranc, Céline Barreteau, Gustavo Mata Osoro, et al.. Effect of the sintering method on microstructure and thermal and mechanical properties of zirconium oxophosphate ceramics Zr 2 O(PO 4 ) 2. Journal of Physics and Chemistry of Solids, Elsevier, 2017, 111, pp.304-310. 〈10.1016/j.jpcs.2017.08.008〉. 〈hal-01590780〉

Partager

Métriques

Consultations de la notice

58